6150 SUP10 1.8159 50CrV4 50CrVA
|
|||||||||
component
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Mo
|
V
|
minimum value
|
0.47
|
-
|
0.7
|
-
|
-
|
0.9
|
-
|
-
|
0.1
|
Maximum value
|
0.55
|
0.4
|
1.1
|
0.025
|
0.025
|
1.2
|
0.4
|
0.1
|
0.25
|
GB
|
ISC
|
CNS
|
JIS
|
KS
|
ASTM/AISI
|
UNS
|
ISO
|
DIN EN/DIN
|
W-Nr.
|
50CrVA
|
A23503
|
SUP10
|
SUP10
|
SPS6
|
6150
|
G61500
|
51CrV4
|
51CrV4
|
1.8159
|
GRADE
|
SIZE(MM)
|
GRADE
|
SIZE(MM)
|
8#-10#
|
∮16-290
|
65Mn
|
∮40-300
|
15#
|
∮14-150
|
45Mn2
|
∮18-75
|
20#
|
∮8-480
|
60Si2Mn
|
∮16-150
|
35#
|
∮8-480
|
20CrMnTi
|
∮10-480
|
45#
|
∮6.5-480
|
20crmnTiB
|
∮16-75
|
Q235B
|
∮6.5-180
|
GCr15
|
∮16-400
|
40Cr
|
∮8-480
|
ML35
|
∮8-150
|
20Cr
|
∮10-480
|
T8-T13
|
∮8-480
|
42CrMo
|
∮12-480
|
Cr12
|
∮16-300
|
35CrMo
|
∮12-480
|
Cr12MoV
|
∮16-300
|
20CrMo
|
∮12-300
|
3Cr2W8V
|
∮16-300
|
38CrMoAL
|
∮20-300
|
45Cr50Cr
|
∮20-300
|
5CrMnMo
|
∮20-450
|
20CrMnMo
|
∮20-300
|
16Mn(Q345B)
|
∮14-365
|
40Mn2
|
∮28-60
|
50Mn
|
∮40-200
|
35Cr
|
∮55
|
15CrMo
|
∮20-75
|
15Mn
|
∮32∮170
|
25#
|
∮16-280
|
40CrMnMo
|
∮80-∮160
|
YF45MnV
|
∮28-80
|
20CrMnMo
|
∮20-300
|
30#
|
∮6.5-480
|
27 SiMn
|
∮20-350
|
30Crmo
|
∮28
|
Crwmn
|
∮20-300
|
30CrmnTi
|
∮16-300
|
H13(4Cr5MoSiVi)
|
∮20-300
|
60#
|
∮210.∮260
|
40crNimo
|
∮20-400
|
Heat treatment or condition
|
tensile strength
σb
Mpa |
Yield point
σs Mpa |
Elongationδ
% |
Reduction of area
ψ
% |
hardnessHBW
|
Impact absorbed energy
KV2
J |
+QT
|
1350~1650
|
≥1200
|
≥6
|
≥30
|
-
|
≥8
|
+S
|
|
-
|
-
|
-
|
≤280
|
-
|
+A
|
|
-
|
-
|
-
|
≤248
|
-
|
+AC
|
|
-
|
-
|
-
|
≤230
|
-
|
+QT=quenching and tempering;+ S=cold shear treatment;+ A=Softening annealing;+ AC=spheroidizing annealing Quenching and hardening temperature 850 ° C ± 10 ° C, oil cooling, tempering temperature 450 ° C ± 10 ° C;
|
Fnish | Definition | Application |
2B | Those finished, after cold rolling, by heat treatment, pickling or other equivalent treatment and lastly by cold rolling to given appropriate luster. | Medical equipment, Food industry, Construction material, Kitchen utensils. |
BA/8K mirror | Those processed with bright heat treatment after cold rolling. | Kitchen utensils, Electric equipment, Building construction. |
NO.3 | Those finished by polishing with No.100 to No.120 abrasives specified in JIS R6001. | Kitchen utensils, Building construction. |
NO.4 | Those finished by polishing with No.150 to No.180 abrasives specified in JIS R6001. | Kitchen utensils, Building construction, Medical equipment. |
Hairline | Those finished polishing so as to give continuous polishing streaks by using abrasive of suitable grain size. | Building Construction. |
NO.1 | The surface finished by heat treatment and pickling or processes corresponding there to after hot rolling. | Chemical tank, pipe. |
It has high endurance strength and creep strength at high temperature, good impact toughness at low temperature, good hardenability, no overheating tendency, small quenching deformation, acceptable plasticity at cold edge forming, and medium machinability. Due to poor weldability, preheat before welding, heat treatment after welding and stress relief are generally used after quenching and tempering, or after high and medium frequency surface quenching or quenching and low and medium temperature tempering. Used as important structural parts working under high load, such as transmission parts of vehicles and engines; The rotor, main shaft, transmission shaft with heavy load, and large section part 34CrMo4 of steam turbine generator are used to manufacture forgings with higher strength and larger quenched and tempered section than 35CrMo steel, such as large gear for locomotive traction, supercharger transmission gear, rear axle, connecting rod and spring clip with heavy load, and 34CrMo4 can also be used for drilling pipe joints and fishing tools for oil deep wells below 2000m
Packaging |
1. by bundles, each bundle weight under 3 tons, for small outer diameter steel bars, each bundle with 4 - 8 steel strips. 2. after making by bundle, covered with Polyethylene waterproof cloth. 3. make black paints painting on each bar, then make bundles |
20 feet container contains dimension | Length under 6000mm |
40 feet container contains dimension | Length under 12000mm |
By bulk vessel | Freight charge is low by bulk cargo, and large heavy sizes can not be loaded into containers can shipping by bulk cargo |
1. Who are we?
Our headquarter is located in Shandong, China. Since 2022, we have sold to North America (60.00%), Western Europe (14.00%) and South America (6.00%). There are about 11-50 people in our office.
2. How do we guarantee quality?
Always provide pre-production samples before mass production;
Always carry out final inspection before shipment;
3. What can you buy from us?
Copper, aluminum, die steel, titanium, customized machine parts
4. Why should you buy from us instead of other suppliers?
The company has 25 years of production experience. It has advanced precision production equipment, modern large warehouse, 200000 tons of inventory goods and a number of long-term stable cooperative customers.
5. What services can we provide?
Accepted delivery conditions: FOB, CFR, CIF, EXW
Accepted payment currency: US dollar, Euro, Japanese yen, Canadian dollar, Australian dollar, Hong Kong dollar, British pound, RMB, Swiss franc;
Accepted payment type: T/T, L/C, D/P D/A, PayPal;
Optional ports: Tianjin, Shanghai, Guangzhou;
Spoken: English, Chinese
6. How can we get your price?
A. We need the following information to quote for you:
1). Product Name
2). standard
3). Material grade (chemical composition)
4). dimension
5). amount
6). Special part drawin
Suppliers with verified business licenses